Two-Part Epoxies

Products

Adesivi a due componenti

USE
Two-part engineering adhesives provide high strength, structural joints. They are suitable for
bonding metals, ceramics, wood and some plastics and they are supplied in a pratical dual
cartridge dispenser. Curing occours upon mixing of the two components (resin and hardener).
Fixture time is from 5 - 10 minutes to several hours. Applying heat will accelerate the cure speed.
Temperature resistance is between - 30 C and + 80 C.

TECHNICAL INFORMATION

Adesivi due componenti
 

TWO PARTS EPOXY ADHESIVES

31-10

Multipurpose, transparent structural adhesive. Recommended for structural bonding of many materials: metals, ferrite, ceramic, marble, glass, concrete, wood and some plastics (polyester, ABS, rigid PVC). Not indicated for rubber, soft materials, polyethylene, polypropylene and PTFE.

Bondings are well resistant to water, gasoline and oils.

31-40

Multipurpose, transparent structural adhesive, fast setting time. Recommended for structural bonding of many materials : metals, ferrite, ceramic, marble, glass, concrete, wood and some plastics (polyester, ABS, rigid PVC). Not suitable for soft materials, polyethylene, polypropylene and PTFE. Bondings are well resistant to water, gasoline and oils.

31-42

Multipurpose transparent structural adhesive, fast setting time. Recommended for structural bonding of many materials : metals, ferrite, ceramic, marble, glass, concrete, wood and some plastics (polyester, ABS, rigid PVC). Not suitable for rubber, soft materials, polyethylene, polypropylene and PTFE. Bondings are well resistant to water, gasoline and oils.

32-43

Multipurpose, thixotropic transparent and flexible structural adhesive, fast setting time. It is designed to be non-sagging for ease of use on vertical surfaces. Recommended for structural bonding of many materials: metals, ferrite, ceramic, marble, glass, concrete, wood and some plastics (polyester, ABS, rigid PVC). Not suitable for soft materials, polyethylene, polypropylene and PTFE. resistance to water, gasoline and oils.

34-15

Highly flexible structural adhesive with improved peeling adhesion and shock resistance. Recommended for bonding of many materials : metals, ferrite, ceramic, marble, glass, concrete, wood and some plastics (polyester, ABS, polycarbonate). Not suitable for PE, PTFE and silicon. Bondings are well resistant to water, gasoline and oils.

35-44

Multipurpose, transparent colourless structural adhesive. It provides a flexible film with good adhesion and peeling strength on metal substrates.
It is recommended for structural bonding of many materials: metals, ferrite, ceramic, marble, glass, concrete, wood and some plastics (polyester, ABS, rigid PVC). Not suitable for soft materials, PE, PP and PTFE. Bondings are well resistant to water, gasoline and oils.

36-10

Multipurpose highly-toughened structural adhesive. Recommended for structural bonding of many materials: metals, ferrite, ceramic, marble, glass, concrete, wood and some plastics (polyester, ABS, rigid PVC). Not indicated for rubber, soft materials, PE, PP and PTFE. Bondings are well resistant to water, gasoline and oils.

3636

Thixotropic two-components adhesive based on epoxy resin, which cures at cold or sparing temperatures. Its specific for bonding of metals, ceramics, woods, foamed materials, many plastics and composites. It provides strong adhesion and high resistance to impact, shocks and vibration. It allows large-size pieces positioning.

4401

Loxeal 4401 is a toughened, semi-flexible, high-temperature resistant, two-part epoxy resin, which provides good adhesion on a variety of substrates as wood, metal, ceramics and many types of plastics and composites. Mixing ratio 2:1 by volume. It provides a strong adhesion with high peel, cut and shear strength up to +120C temperature with peaks at +140C. Excellent resistance at high temperature for short periods, as i.e. in stove enamelling cycles.

4428

Loxeal 4428 is a thixotropic, two-components epoxy resin. Especially developed for composites bonding, it provides excellent impact and vibration as well as high temperature resistance. Its ease of mixing and applications allows its use on gap filling.

4429

Loxeal 4429 is a toughened, semi-flexible, high-temperature resistant two-component epoxy resin. Especially developed for composites bonding, it provides good adhesion on various substrates as wood, metal, ceramics and many types of plastics. Designed to be nonsag for ease of use on vertical surfaces and in wide gaps. Mixing ratio 2:1 by volume. It provides a strong adhesion with high peel, cut and shear strength up to +120C temperature with peaks at +140C.